Stainless steel 904l round bar manufacturer and exporter

Mukesh Steel India is engaged in offering wide range of Stainless Steel 904 L Round Bars that is widely demanded in several industries.

904L is a high-combination austenitic stainless steel with low carbon content. The evaluation is expected for use under extreme destructive conditions. It has been application demonstrated over numerous years and was initially created to oppose erosion in weaken sulfuric corrosive.

Basically, 904 L is completely austenitic and is less delicate to precipitation ferrite and sigma stages than customary austenitic evaluations with high molybdenum content. Typically, because of the blend of moderately high substance of chromium, nickel, molybdenum and copper 904L has great imperviousness to general consumption, especially in sulfuric and phosphoric conditions.

Standard	SS 904L
UNS	N08904
WERKSTOFF NR.	1.4539
JIS	SUS 904L

Specification

Standard	904L / 1.4539
Range	3.17mm to 350mm dia
Designation	ASTM A276, ASME SA276
Finish	Bright, Black, Polish, Export Bright
Thickness	4.0mm - 100mm
Type	Bar, Bright Bar, Black Bars, Hex Bar, Square Bar, Rods, Polish Bar, Forged Bar, Round Bar
Length	Random, Fix & Cut Length

Chemical Composition

Grade	C	Cr	Cu	Mn	Mo	Ni	P	S	Si
904L	Max			Max			Max	Max	Max
904L	0.02	19.0-23.0	1.0-2.0	2.0	4.0-5.0	23.0-28.0	0.045	0.035	1.0

Mechanical Properties

Density	8.0 g/cm3
Melting Point	1454 °C (2650 °F)
Tensile Strength	Psi – 75000 , MPa – 515
Yield Strength (0.2%Offset)	Psi – 30000 , MPa – 205
Elongation	35 %

TYPES OF STAINLESS STEEL 904L ROUND BARS & RODS